re boulder formation

Hi Silastman Its really hard, you see. We have to use the analogue of mighty mouse as you saying but after re...

re boulder formation

Hi Ted Yes its really clinker ball which forming in smokebox as you suggest. So I think there is one change s...

re boulder formation

Hi  Here is chemical composition of the boulder, what do you think about this? might be it made from the midl...

re boulder formation

Hi Ted Your suggestion is  absolutely useful. I will try and see what happen. So thanks for your help. Wi...

re boulder formation

Hi Ted we have no problem with the free lime (~1.0) and volatility (~0.8) in operation but the yellowish-brow...

boulder formation

Dear sir We're facing a problem that lead to stop the kiln. Too many big ball clinker form in operation. So wha...

re Re: 28 days strength

Actually the PSD also influence on cement strength, especially the 28days right? but how to define it?

re red spot on kiln shell

Yes we tried to control smoothly to form coating there (but do not change too much feed, fuel and speed). If in ca...

red spot on kiln shell

Dear sirs We're facing a serious situation that some red spots had appeared on kiln shell place on 42m positi...

Re: 28 days strength

so it mean we have no exactly solution to predict the late strength. I found some plant have different taget (LSF,......