Dear all I am going to modify the louvre ring of my VRM, cement grinding. I don't know which case as following is b...
Hello ILA At the movement, our clinker is acceptable but we wan to increase its quality by increase C3S. RM parti...
Dear all Our clinker designed with SR 2.5, LS 95.5. C3S according to calculation is arround 58%. If we wan to incre...
It could be by product from power plant (or other processes), we call chemical gypsum or artifical gypsum. It caus...
Dear all Can you please share me what factors impact on Water demand of cement? In my plant, we have a problem with...
Dear Ted Thank you very much for your sharing. This is very useful for us to improve the quality of RM. If anyone ...
Dear all Our plant is using Logitudinal Preblending method to build up the stockpile. As you know this method has p...
Dear all, In my plant, we are trying clinker mineralization for a few days. So far there is no problem with the kil...
Thanks, Ted. Tam
Dear All, Our plant is using High grade limestone as filler for cement grinding. We are going to change the limesto...
;