Re: Bulk density

Sorry to say, but the remark of "Cement supplier" seems completely wrong to me. The density of a packing of partic...

Re: Kiln Shell Red Spot

Any hot spot should in principle not be allowed to reach a temperature superior to 700°C. The reason for this is t...

Re: Use Limestone for Cement Grinding

The European norm EN 197-1 2000 states that the amount of clay in limestone used for the production of blended cemen...

Re: about RSP calciner

Concerning the main burner, a Pillard multichannel should be able to burn anthracite without any problem, so you sho...

Re: Terminology

"A", "B", "C",...,"F" I guess that as the "F" phase was really, really rare, Törnebohm left some place for some 'D"...

Re: Terminology

Because Swedish geologist and mineralogist Alfred Elis Törnebohm lacked imagination. When he investigated the phase...

Re: Increased stack air flow - fuel efficiency?

It seems very unlikely that you could have an increase of heat consumption without having one of the exhaust tempera...

Re: Raw mill drying problem

The only problem I can see is to ensure that enough air can be drafted through your hot gas generator. You should c...

Re: Using industrial waste for cement burning

Frankly, this question is far to broad to be discussed in this forum. You better do a little research on the subjec...

Re: raw meal homogenization

If I understand correctly, you want to start a cycle 20t bunker -> elevator -> 20 t bunker. Due to the very low mas...